White Porland Cement |
 |
|
SAMPLE: WHİTE PORLANT CEMENT
(Average Analysis)
DATE OF REPORT:01.02.2009
|
STANDARD:EN 197-1 CEM I 52,N |
| |
| CHEMİCAL REQUIREMENTS |
RESULTS |
METHODS |
STANDARD VALUES
Min. Max.
|
|
| Loss On Ignition % |
3,24 |
EN 196-2 |
- |
5,00 |
|
| Insoluble Residue% |
0,14 |
|
|
|
|
| Sulfur Trioxide % |
3,65 |
XRF |
- |
5,00 |
|
Soluble Chromium CR ppm |
0,84 |
AAS |
|
- |
|
| Chloride % |
0,0085 |
EN-196-21 |
- |
0,10 |
|
| PHYSICAL REQUIREMENTS |
- |
|
|
|
|
| Degree Of Whiteness % |
85,1 |
CIE SYSTEM Y VALUE |
- |
- |
|
| Initial Setting Time Minute |
105 |
EN 196 1,3 |
45 |
- |
|
|
| Soundness,Lee Chatelier mm |
1,0 |
- |
10,00 |
|
|
| 2 Days Compressive Strength Mpa |
36,0 |
20,0 |
|
|
|
| 28 Days Compressive Strength Mpa |
60,00 |
- |
52,5 |
|
|
|