CERTIFICATE OF ANALYSIS |
 |
|
| DESCRIPTION OF SAMPLE |
:SULPHATE RESISTANCE CLINKER |
| DATE OF PRODUCTION |
: |
| TO |
: |
| B/L QUANTITY |
: |
| VESSEL NAME |
: |
| PARTY NO |
: |
| CHEMICAL ANALYSIS |
VALUES OF ANALYSIS (%) |
|
|
| SiO2 |
21,00 |
|
|
| Al2O3 |
4,56 |
|
|
| Fe2O3 |
5,72 |
|
|
| CaO |
65,89 |
|
|
| MgO |
1,15 |
|
|
| SO3 |
0,72 |
|
|
| Na2O |
0,18 |
|
|
| Loss on Ignition ( LOI ) |
0,51 |
|
|
| Free Lime |
1,07 |
|
|
| Hydrolic Ratio (H.R.) |
2,11 |
|
|
| Silicate Ratio (S.R.) |
2,05 |
|
|
| Aluminate Ratio (A.R.) |
0,80 |
|
|
| Lime Saturation Factory (LSF) |
94,73 |
|
|
PHYSICAL ANALYSlS |
VALUES OF ANALYSlS |
|
|
| Density (g/L) |
1250 |
|
|
| Spesific Surface Area Blaine (cm2/g) |
3378 |
|
|
| Comp. Strength (N/mm2) 2 days |
24,7 |
|
|
| Comp. Strength (N/mm2) 7 days |
42,0 |
|
|
| Comp. Strength (N/mm2) 28 days |
52,7 |
|
|
C3S |
|
=63,38 |
| C2S |
|
=12,48 |
| C3A |
|
=2,40 |
| C4AF |
|
=17,41 |
| 2*C3A+C4AF |
|
=22,21 |
|
|